ITW Philadelphia Resins USA [Vanson Engineering Pvt. Ltd.]

DESCRIPTION:
CHOCKFAST ORANGE (PR-610TCF) is a specially formulated 100% solids, two component inert filled casting compound developed for use as a chocking or grouting material. CHOCKFAST is designed to withstand severe marine and industrial environments involving a high degree of both physical and thermal shock. The compound is non shrinking and has very high impact and compressive strength. Years of successful in-service experience have shown the use of PR-610TCF to be a far superior yet less expensive method of establishing and permanently retaining precise equipment alignment under extreme conditions. PR-610TCF is approved or accepted for its intended marine use by American Bureau of Shipping, Lloyd's Register, Bureau Veritas, Det Norske Veritas, Germanischer Lloyd and most other major regulatory agencies worldwide.

APPLICATION:
CHOCKFAST ORANGE was developed as a chocking or grouting compound for use under marine main propulsion machinery. The compound is used under diesel and gas engines, reduction gears, generators, compressors, pumps, bearing blocks, crane rails and numerous other applications. PR-610TCF requires no special tools or special skills as does chocking with steel. When cast, CHOCKFAST ORANGE flows readily into the chock area filling voids and conforming to all irregularities. This eliminates the machining of base plates or foundations for a perfectly fitted chock.

PHYSICAL PROPERTIES OF CHOCKFAST ORANGE:

COEFFICIENT OF LINEAR THERMAL EXPANSION: Temperature Range: 0°C to 60°C (32°F to 140°F)	30.8 x 10^-6/C° 17.1 x 10^-6/F°	ASTM D-696
COMPRESSIVE MODULUS OF ELASTICITY:	37482 kg/cm² (533,000 psi)	ASTM D-695
COMPRESSIVE STRENGTH:	1336 kg/cm² (19,000 psi)	ASTM D-695 (Mod)
FIRE RESISTANCE:	Self extinguishing	ASTM D-635
FLEXURAL STRENGTH:	575 kg/cm² (8165 psi)	ASTM C-580
FLEXURAL MODULUS OF ELASTICITY:	72880 kg/cm² (1.04 X 10⁶ psi)	ASTM C-580
HARDNESS - BARCOL:	40-44 fully cured 35 minimum	ASTM D-2583
IZOD IMPACT STRENGTH	0.27 Newton m/cm (6 in.lbs./in.)	ASTM D-256
LINEAR SHRINKAGE:	0.0002 mm/mm (0.0002 in/in)	ASTM D-2566
POT LIFE:	30 MIN. @ 21°C (70°F)
SPECIFIC GRAVITY:	1.58
TENSILE STRENGTH:	349 kg/cm² (4,970 psi)	ASTM D-638
COVERAGE:	1966 cc per 3.4 kg (120 cu.in/7.5 lbs.) 4261 cc per 6.8 kg (260 cu.in/15lbs.)
CURE TIME:	48 hours @ 15°C (60°F) 36 hours @ 18°C (65°F) 24 hours @ 21°C (70°F) 18 hours @ 26°C (80°F)
SHELF LIFE:	More than 18 months
SHOCK RESISTANCE:	Pass MIL-S-901C (Navy) High Impact Shock Test, Grade A, Type A, Class 1
SHEAR STRENGTH:	380 kg/cm² (5,400 psi)	FED-STD-406 (Method 1041)
THERMAL SHOCK:	Pass -18°C to 100°C (°F TO 212°F)	ASTM D-746
VIBRATION:	MIL-STD-167

	Propeller Shaft Coating System
PHYSICAL PROPERTIES
COLOUR:	Clear Amber
CURE TIME:	24 hours @ 22°C (72°F)
% ELONGATION:	30% ASTM D-638
FLEXURAL MODULUS:	8050 kg/cm²(1.15 x 102psi)
FLEXURAL STRENGTH:	366 kg/cm ²(5,200 psi) ASTM D-790
MIXING RATIO:	4:3 by volume and weight
SPECIFIC GRAVITY:	1.08
NET WEIGHT per 3.8 liter(1 gallon) Unit	4.1 kg (9 lbs)
PACKAGING:	3.8 liters (1 gallon) unit
POT LIFE:	40 MIN. @ 22°C (72°F) 3.8 liters (1 gallon) unit
SHELF LIFE:	One year
TENSILE STRENGTH:	285 kg/cm ²(4,050 psi) ASTM D-638
VISCOSITY:	1000-1500 cps @ 22°C (72°F)
TAILSHAFT COATING SYSTEM	PHILLYBOND #6 - Repair and Patching Compound
SUPER ALLOY TITANIUM REPAIR COMPOUND - Machinery Repair Alloy	SUPER CERAMIC REPAIR PUTTY - Highly Abrasion and Erosion Resistant Surfacer
Chockfast Orange for Slew ring bearing application Chockfast orange provide accurately cast races for large diameter bearing

1	Superior permanent alingnment...assures a significant reduction in damage to crankshafts, crankcases and bearings.
2	Precise & unsurpassed contact with bedplates...without costly machining.
3	Free flow of air under hot-running machinery...reduces foundation "humping" problems.
4	Fast, convenient installation without any time-consuming, expensive hand-fitting...minimal equipment downtime.
5	Resists degradation by fuels, lubricants & fires...no possibility of freeting or corrosion.